Armanios 10. International Congress on Metallic Corrosion Part 1

Erscheinungsjahr 1988
ISBN: 978-3-0357-0319-1
Verlag: Trans Tech Publications
Format: PDF
Kopierschutz: 0 - No protection

E-Book, Englisch, 4220 Seiten

These five volumes present approximately 500 contributions from 33 countries, the majority coming from Western Europe, USA, Japan, China and India.

Autoren/Hrsg.

Armanios, Erian A.

Inhaltsverzeichnis

Atmospheric Corrosion in Marine Environments
A Simulative Laboratory Test for Evaluation of Metallic Corrosion in Windy Coastal Atmosphere
Long-Term Atmospheric Corrosion of Mild Steel, Zinc, Copper and Aluminium in Spain
The Atmospheric Corrosion Study of Galvanized Steel Wire Strand in Taiwan
Corrosion Mapping for Catalonia, Spain
Application of Metallography to the Determination of Aluminium Corrosion in Different Test Sites in Galicia (N.W. of Spain)
Study of Behaviour of Several Zinc Coatings in Atmospheres Containing Sulphur Dioxide
The Pitting Factors of Low Carbon Steel: Correlation between Accelerated and Atmospheric Corrosion Testing
A Study of Rust Layer of the Atmospheric Corrosion-Resistant P-V System Low Alloy Steel
Application of Infrared Spectroscopy in the Study of Atmospheric Rust Systems
Removal of the Corrosive Hydrogen Sulfide Pollutant from the Intake Air for a Controlled Environment
Utilisation of Weathering Steels in Czechoslovakia
Chloride Ion Effect on Aluminium under Atmospheric Corrosion Conditions
The Morphology of Corrosion Products on Steel
Effect of Air Pollution on Corrosion of Mild Steel: Preliminary Field Studies at Three Sites in Madras City
Atmospheric Corrosion of Metals - Long Term Exposure Results at Mandapam Camp
Atmospheric Testing of Metallic Coatings
Corrosion of Structural Metals in Atmospheres with Different Corrosivity at 8 Years' Exposure in Sweden and Czechoslovakia
Corrosion of Metals in Sulphur Dioxide Atmosphere - A Laboratory Study
Atmospheric Steel Corrosion in Industrial Zone of Pancevo
Temperature Influence of Corrosion of Armco Iron in Acid Solutions
The Mechanism of Tensile Stress Accelerating Anodic Dissolution of Metals
Cathodic Polarization of Vapour Deposited Aluminium Film Electrodes in HCI Medium
Pourbaix Diagrams Derivation in the Presence of Polynuclear Species in Solution
The Study of the Particle Size of the Inner Rusty Layer of Seawater Corroded Products of Low Alloy Steel
Corrosion of Steels in the H2O-H2S System: Protective Properties of Corrosion Film
The Anodic Dissolution of Iron XII. Recent Findings Supplementing the Information about the Kinetics of the Dissoluion Reactions
Electrochemical Behaviour of Copper-Nickel Alloy in Sodium Chloride Solution
Features of Electrochemical Noises during Pitting Corrosion
The Erosion Corrosion Behavior of Cu-Ni Alloys in Synthetic or Natural Seawater from Potential and Impedance Measurements
The Effect of Copper-Addition on Electrochemical Behavior and Surface Composition of Ferritic Stainless Steel in Sulfuric Acid Solution
The Study of Anodic Behaviour of Ni-P Alloy in Chloride Solution
An Electrochemical Investigation of the Corrosion Behaviour of Mild Steel in Clay
Electrochemical Behaviour of Aluminium in NaCl-Anodic Polarisation in Alkaline Solutions
Partial Electrochemical Reduction of Thin Oxide Film Grown on Stainless Steel Nb Alloys
Electrochemical Corrosion of Copper and Copper Sulphide in Acidic Solutions
Oxidation and Corrosion of AlSi 304 Study by Cyclic Voltammetry, Potentiostatic, Galvanostatic and Impedance Methods
Peculiarities of the Electrochemical and Corrosion Behaviour of Metals (Fe, Al) in Aprotic Media
Electrochemical and Corrosion Behaviour of Zr-Based Intermetallic Compounds
Electrochemical Behaviour of Copper-Nickel Alloy in Sulfide Polluted Sea Water
Thin Layer Mixed Potential Model for the Corrosion of High Level Nuclear Waste Canisters
Mass Transfer Aspects of Electrochemical Corrosion
Corrosion Behaviour of Titanium Anodic Oxide Films
Electrochemical Aspects of Selective Sulphide Mineral Dissolution
Zinc Behavior in Slightly Alkaline Solutions the Reduction Processes
Development of the Theory of Structural Electrochemical Corrosion of Metals and Alloys
Corrosion Behaviour of Sintered Stainless Steel in Sulphuric Acid and Sodium Chloride Solutions
Dynamic System Analysis in Corrosion Research and Testing
Corrosion in Ferric Chloride Solutions Evaluation by D.C. Electrochemical Methods
Corrosion-Electrochemical Properties and some Aspects of the Electronic Structure of Chromium Carbides, Nitride and Carbo-Nitrides
Hydrogen Evolution Kinetics in Corrosion of Copper, Iron and Zinc in Water
Chemical Corrosion of Silver in Silver Nitrate Containing TiO2 and Alkaline Earth Metal Ions
Electrochemical Polarization Studies of API 5L Grade X65 Steel in Chloride Solution
Studies on Bimetallic Corrosion
A Unified View of the Formation and Growth Phenomena of Oxides on Uniform Metal Electrodes
Mechanism of Tin Dissolution in Sulphuric Acid
Optical Study of Copper-Inhibitor System
Mechanism of Oxygen Reduction of Stainless Steel
Corrosion and Diffusion
Cathodic Polarisation in Aqueous Solutions
Influence of Crystallization on Corrosion of Fe-Ni-B Metallic Glasses
Effect of Chloride Content in Industrial Water on Corrosion Behaviour of Steels
Mechanistic Studies on the Dissolution of Copper in Sulphuric Acid and Hydrochloric Acid
Corrosion and Electrochemical Behaviour of Tungsten Carbide in Phosphoric Acid at High Temperature
Electro Chemistry of Cr- and Ni-Base Binary Metallic Glasses
Electro Chemical Behaviour of Porous Nickel Electrode in Alkali Solutions
Nucleation and Growth of Anodic Films IV. Anodic Deposition of Silver Sulphide
Galvanic Corrosion at Composite-Metallic Materials Interface
Corrosion Studies of Zinc in Aqueous Binary Mixtures of Acetonitrile through Polarisation Technique
Electrochemical and AES Investigation of some Metallic Glasses in Sulphuric Acid Solution
Corrosion of 7075 Al Alloy in Media Contaminated by Cladosporium Resinae
Steel Corrosion by Metabolic Products of Sulfate Reducing Bacteria Prevention by Inhibitor
Microbiological Corrosion of Steel in the Water of Thermal Power Plant
The Influence of Bacteria of Sulphur Cycle on Lead Corrosion
Microorganisms as Factors of Damage of Gas Pipe-Lines Coverings
Ecological and Biochemical Aspects of Corrosion of Underground Constructions
Changes in the Composition of Microbial Communities in the Process of Corrosion of Reinforced Concrete Constructions
Mechanisms and Control of Microbiological Corrosion in Petroleum Industry
Anti-Corrosive Properties of Spent Motor Oils
Case Study of Corrosion in Desalination Plants
Case Study: Development Motor Vehicle Underbody Coatings in Yugoslavia
Corrosion and its Protection of Evaporator's Red Copper Heating Pipe in Chemical Production of Salt
Corrosion Behaviour and Stress State of Laser Hardened Zone on Spring Steel
Failure of Copper Pipes in Kuwait's Domestic Tap Water
Corrosion and Material Problems in Cogeneration Boiler Systems of the Pulp and Paper Industry
Electrochemical Aspects of Grinding Ball-Mineral Interactions in Ore Grinding
Electrochemical Study of the Corrosion Resistance of Copper and some Brazingsin Hot or Cold Domestic Water
Applicability of Electrochemical Impedance Technique in Metallic Sheets Quality Control for Food Industry
Corrosion Experience with a Large Vehicle Fleet
Stess Corrosion Cracking of Ammonia Storage Sphere
The Exploitation of Low Temperature Heat
Fly Ash Erosion Behaviour of Boiler Tube Materials in the Coal-Fired Boiler Environment
High Temperature Corrosion of Cast Iron Chains by Coal Ash
Case Study of Stress Corrosion Cracking of Stainless Steel Tubes due to Continuous Chlorination Treatment of Cooling Water
Use of Organo-Phosphonate Cooling Water Treatment in Indian Chemical Process Industries
Electrochemical Evaluation of Dissolution Characteristics of Al-Basic Sacrificial Anodes in Seawater
Vertical Semi-Continuously Cast Aluminum Anodes, Further Improvements
Optimization in Anode Arrangements in High Electric Resistance Media
Cathodic Protection Economics as Related to Graphite Anode Behaviour in Deep Groundbed Systems
Electrochemical Behaviour and some Examples of Application of PbO2/Ti Electrode in Sea Water with Different Salinity
Mathematical Modelling of Electrochemical Protection
Protection of Steel by Inhibitors in Combination with Impressed Current
Experimental Confirmation of a Mathematical Model for the Design of Cathodic Protection Systems
Development of a Series of Al-Zn-In Ternary Alloy Anodes for the Cathodic Protection of Submerged Structures
Studies on Mg Alloys Containing Mn for Use as Galvanic Anodes
The Dissolving Mechanism of Aluminium Anodes in Chloride Solution
Aluminium Alloy Anodes for Cathodic Protection of Marine Structures
Micro-Computer Controlled Cathodic Protection System
Corrosion and Cathodic Protection of Ice Going Vessels in Subarctic and Arctic Environment
Performances of Various Anodes Used in the Impressed Current Cathodic Protection System
Performance of Aluminum Alloy Anode in High Temperature Sea Mud
Corrosion Preventive Coatings on Aluminium
Considerations on the Corrosion Resistance of Metallic Materials Coated with Electroless Nickel
Status of Protective Coating and Lining in the Industry in India - an Overview
Effect of Deposition Temperature on Microstructure and Corrosion Resistance of Tantalum Coating
Corrosion of Metal Beneath Coatings
Influence of Thinner Addition on Brushability and Sagging of High Build Anticorrosive Paints
A Study of the Relation between Ion Beam Etching and Chemical Etching of Aluminium Thin Films Prepared at Different Experimental Conditions
Corrosion Resistance of Tantalum Coating in Fused Salt
Evaluation of Anticorrosive Paint Binders by Mean of A.C. Techniques Influence of the Coat Thickness
On Electrochemical Reductive Destruction and Cathodic Disbondment of Protective Polymeric Coatings
Effect of some Factors on the Poymeric Coatings-to-Cathodic Disbonding Stability
Cathodic Process of Atmospheric Corrosion and an Approach to Development of Rust Control Coating
Factors Influencing the Corrosion Resistance of Polyster Powder Films on Zinc Coated Steel
Study of Different Primers in Natural Environments
Antifouling Paints of the Emulsion Type Based on Cuprous Oxide
Investigation of Degradation Processes in Primer Coatings
Surface Enrichment of Mild Steel and Cast Iron with Silicon (by a C.V.D. Process) and Corrosion Behavior of Coated Materials in Hot Concentrated Sulfuric Acid
Influence of Curing Process Parameters on the Quality of Organic Coatings
Effect of Phosphorus on the Structure and Corrosion Behaviour of Electrodeposited Co-P Films
Study of Titanium Anodization by Means of O18 Tracing and Ion Beam Analysis Techniques
The Technology and Practice in Production of Hot Dip Galvanised Steel Pipes by the Slight Oxidation Reduction Process
A Study on Ni-P Amorphous Electrodepositing Process
The Water Content and Transport through Chlorinated Rubber Hydrophobic Free Films
The Salt Content and its Transport through Epoxy-Polyamide Hydrofobic Free Films
Electrochemical Measurements of Corrosion Beneath Organic Coatings
Some Aspects of the Application of Electrochemical Measurements for the Assessment and Selection of Zinc Rich Primers
Limitations and Possibilities of the Typical Electochemical Impedance Measurements for Studying Anti-Corrosive Paint Coatings
Studies on Corrosion of Electroless Nickel
The Corrosion Behaviour of Low Alloyed Electroplated Zinc Layers
The Influence of Operating Conditions on the Behaviour of Coatings Exposed to Petroleum Fluids
Studies on Non-Aqueous Phosphating
Evaluation of Corrosion Resistance of Electrodeposited Chromium
Corrosion Behaviour of Nitrided Steels in Sodium Chloride Solutions
Electronoptical Investigation of the Inhibition of Corrosion of Mild Steel in the Presence of Paint Films Containing Zinc Chromate
The Effect of Laser Surface Treatment of High-Temperature Oxidation and Corrosion Resistance of Materials and Coatings
Evaluation of Zinc Electrodeposits for Corrosion Resistance
Effect of Anions of the Formation of Chromate Film on Zinc
Characteristics of Ni-Al2O3 Electrodeposited Composites
Corrosion Resistant Precoated Autobody Steel Sheets
Performance of Electroless Nickel-Tungsten Alloys
Electrodeposition of Acrylic Resin from Water Soluble Systems
Development of an Acrylic Coating for Corrosion Protection
Water Borne Coatings Based on Polyester for Corrosion Protection of Metals
Evaluation of Organic Coatings by Impedance Studies
Cathodic Electrocoatings from Epoxy Based Paints
Electrodeposition of Corrosionstable Zinc Alloyed with Aluminium
Evaluation of Organic Coatings on Pretreated Aluminium Alloys
Chromizing of Steel Reinforcement Bars
Hot Corrosion of NiCoCrAlYTa Coatings
The Corrosion Behaviour of Titanium Nitride Coatings in Dilute Acid Solutions
Studies of Aluminium Diffusion Treated Steel for Heat Exchanger Tubes
Change of Structure and Chemical Composition of AlZn5Mg3Cu1.5 Alloy during the Process of Anodizing in Sulphuric Acid
Cadmium Deposition from Perchloric Acid Based Electrolyte
Investigation on Cathodic Disbonding of Chlorinated Rubber Coating on Mild Steel
Investigations of the Factors Affecting the Adhesion of Chlorinated Rubber on Mild Steel Using Modified Blister Technique
The Influence of a Fluoride Film on the Corrosion Resistance of Aluminium Heat Exchangers Fabricated with a Fluoride Flux
Corrosion Fatigue of Steels for Prestressing Concrete
Electro-Chemical Behaviour of Coated Reinforcement in Cement Concrete
Study of Metallic Corrosion of Tubing in Buildings. Evaluation by A.C. and D.C. Techniques
Studies on Corrosion Resistance of Sulphur Concrete
Application of Impedance Technique to Study the Corrosion Behaviour of Steel in Concrete
Deterioration of Concrete in Industrial Environments
Corrosion of Steel in Concrete Studied by Electrochemical Impedance Measurements: Application to the Monitoring of Concrete Structures
Corrosion Processes at Concrete/Iron Electrode
Accelerated Testing of Zirconium and its Alloys Resistance for Specific Types of Corrosion
Effect of Hydrochloric Acid Vapours at Room Temperature on the Oxide-Sulphide Scales on Fe-Cr-Ni Alloys
Aqueous Corrosion of U3O8-Al Cermet Cores
On the Corrosion Characteristics of some Modified Aluminium Alloys in Sea Water with Different Pretreatments under Dynamic and Nearly Static Conditions
A Study of the Corrosion Processes of Low Alloy Steels in Artificial Sea Water
The Influence of Niobium on the Oxidation of All-Austenite Stainless Steels
Influence of Rare Earth Metals Y, Ce and La on the High Temperature Sulfidation of Fe-25Cr-40Ni Superalloy
The Influence of Pb, Fe, Mg Alloying Impurities on the Corrosion Behaviour of A1-Brass Alloys
Corrosion of Molybdenum - Containing Amorphous Iron Alloys
Selective Corrosion of Brasses
Improvement of Corrosion Behavior of Cast Iron for Sulfuric Acid Concentration Plants by Modification of Composition and Structure
Corrosion-Resistant High-Chromium, Titanium, Molybdenum, Ruthenium or Palladium Alloyed Steels
Influence of Heat Treatments on the Corrosion Resistance of Cr-Co Dental Alloys
Duplex Stainless Steels the Cost Effective Answer to Corrosion Problems of Major Industries
Corrosion Kinetics Study of Sintered Fe/8% wt Cu by Means of Electrochemical Methods
Tarnishing and Corrosion of Semi-Precious Alloys for Dental Applications
Rapidly Quenched Pb-Sb, Pb-Sb-Sn Alloys Preparation and their Physical and Corrosion Resistant Properties
Effect of Aging on the Hardness and Corrosion Resistance Properties of Fe82B10Si8 Metallic-Glass
The Behaviour of High-Alloy Steels in Flue Gases
Mathematical Modeling for Carbon Diffusion and Carbide Precipitation in NiCr-Based Alloys
Corrosion Behaviour of Duplex Steel Obtained by Electron Beam Treatment of AlSi 304
Studies on the Behaviour of Lead-Antimony-Silver Alloy under the Influence of A.C. Superimposition
Analysis of Cost of Corrosion in Industry and Saving due to Adoption of Corrosion Control Measures
The Nace-NBS Corrosion Data Program
Mastering Process Industry Corrosion Problems: Anti-Corrosion Measures as Part of Plant Maintenance System
On Loading Mode (I, III) Technique as a Means of Determination of Crack Growth Mechanism in Stress-Corrosion Cracking
Texture-Based Computer Modelling of Environmentally Induced Cleavage in Hexagonal close Packed Metals
Stress Corrosion Test Method Using Self-Restraint Small-Size Specimens
Stress Corrosion Cracking in Steels Used for the Manufacture of Nonmagnetic Drill Collars
Liquid Metal Corrosion under Constant and Cycling Stress
Effect of Temperature, Concentration of Medium and Potential on Intergranular Stress Corrosion Cracking of Mild Steel in NaNO3 Solution
Resistance of Aluminized Steel to Environmental Corrosion
Relations between the Non-Sensitized Intergranular Corrosion and the Potentials and Test Method of its Susceptibility for 316L Stainless Steel
Electrochemical Conditions at the Crack Tip and Crack Propagation Rates during Corrosion Fatigue of Steel in Deaerated Sea Water
Critical Conditions for High Alloys in Sour Gas Environments
Role of Microadditions of Boron in Intergranular Corrosion of Austenitic Stainless Steels
Effect of CaCl2 Concentration on the Probability Distribution of Stress Corrosion Cracking Failure Time of Type 304 Stainless Steel
Intergranular Stress Corrosion Cracking of Sensitized AlSi 304 by Fluoride Ions and its Inhibition
The Relationship between CrNi 18-10 Austenitic Stainless Steel Intergranular Corrosion and the Linear Welding Energy
Co2 and H2S Environments Resisting Steels
Evaluation of Resistance to Intergranular Corrosion of Stabilized Stainless Steels
The Surface Morphologies of Crack during Stress Corrosion Crack Propagation
Research on Acoustic Emission Characteristic and Mechanism of Stress Corrosion Cracking
An Investigation into the Fretting-Corrosion-Fatigue of High Strength Steel Wire
The Fretting of Stainless Steels in Selected Corrosive Environments
Corrosion Fatigue Behaviour of Austenitic Stainless Steels
Effect of some Extraneous Ions on the SCC Susceptibility of AlSi 304 SS in Polythionic Acid
Stess Corrosion Cracking of Mild Steel in a Cooling Water System due to Nitrobacteria
Stess Corrosion Cracking of Soft Martensitic CrNi Steel Grade G-X5CrNi134 as a Function of its Heat-Treatment Condition
Effect of Residual, Impurity Elements and Microstructure, on the Mechanical Properties and the Crack Growth Rate in Delayed Failure Test of Martensitic Fe-Ni Alloy
Stess Corrosion Testing of Al-Zn-Mg Alloys
The Intergranular Corrosion Resistance of 17% Cr Ferritic Stainless Steels when Overheated
Electrochemical Study of the Corrosion Fatigue of Low Alloy Steels in Aqueous Solutions Containing Carbonate-Bicarbonate Ions
Stress Corrosion Cracking of High Strength Al-Cu-Mg-Si Alloys after Two-Step Aging
The Effects of Stress Ratio on Corrosion Fatigue Crack Growth of a High Strength Steel
Effect of Environmental Media on Stress Corrosion Cracking of High Strength Steel 37 SiMnCrMoV
Stress Corrosion Cracking of Welded Joints in Caustic and Nitrate Solutions
Subcritical Propagation of Sc-Crack of Welded Joints in Caustic and Nitrate Solutions
Some Studies on Stress Corrosion Cracking in Plain Carbon Steels
Effect of Solution Concentration on Stress-Corrosion Cracking of Mild Steel in Phosphate Medium
Constant Strain Rate Test of SCC of Type 18/8 Ti Austenitic Stainless Steel in Boiling 45wt% MgCl2 Solution
Effect of Microstructure on Electrochemical Polarization and SCC of Eutectoid Steels
The Relation between Stress Corrosion Cracking and Hydrogen Embrittlement
Stress Corrosion Cracking of Carbon Steel in Amine Units
Corrosion Behavior of an AlSi 304 Stainless Steel Hip Treated
Slow Strain Rate Test Applicability for Sulphide Stress Corrosion Cracking Study of High Alloyed Stainless Steels for Oil Wells
Stress Corrosion Cracking of High Strength Prestressing Steel in Na2HPO4 Medium
Investigation on some Factors Influencing Propagation of SCC of 18-8 Austenitic Stainless Steel in the Medium Containing Cl-
Significance and Integration of Creep Deformation Modeling in the Quantitative Evaluation of Intergranular SCC at Moderate Temperature
Influence of Potential and pH on the Stress Corrosion Cracking of a Duplex Stainless Steel in Chloride Solution
Influence of Externally Applied Stresses on Pure Nickel in a Dry, Sulphidizing Environment
Effect of Ageing at 973k on the Stress Corrosion Cracking Behaviour of Type 304 Stainless Steel in Boiling MgCl2 Solution
Evaluation of Susceptibility to Stress Corrosion Cracking (SCC) in Sodium Chloride Solution of Weldments of Cold Rolled Type 316 Stainless Steel
Hot Salt Stress Corrosion Cracking of a Titanium Alloy: The Phenomenon in View of Aero Gas Turbine Operating Conditions
The Influence of Carburizing and Decarburizing Environments on the Creep Behaviour of Ni-22Cr-9Mo-12Co-1Al
Effect of Strain Rate on the Stress Corrosion Crack Behaviour and Mechanical Properties of Stainless Steel in Hot Magnesium Chloride
Prediction of the Onset and Time-to-Failure for Hydrogen Stress Cracking of Line-Pipe Steel
Environmental Effects on High Temperature Crack Growth
Anomalous Isotope Effects during Hydrogen Embrittlement of Structural Materials in Electrolytes
Hydrogen Pick-up during Corrosion of Steel: Influence of Inhibitors and Promoters
A Study of Alkali Embrittlement Cracking of Low Carbon Steel Welded Joints
Hydrogen Induced Cracking Susceptibility of Low Strength Steels with Different Phosphorus Content in Acid Media
Hydrogen Embrittlement Behaviour of Ni-Nb-Cr and Ni-Nb-Al Amorphous Alloys
The Mechanism of Impeding the Hydrogenation of Cathodically Polarized Titanium by Anions of Hypochlorite and Chlorate
The Effect of Minor Additions Mn, Cr, Zr and Ti on the Hydrogen Embrittlement in Al-Zn-Mg-Cu Alloy
Hydrogen Diffusivity in Pure Aluminum by Using Electrochemical Hydrogen Permeation Technique
Effect of Hydrogen on Anodic Behaviour of 304 Stainless Steel
Study on Improving the Resistance of High Strength Steel to Hydrogen Embrittlement
Studies on Hydrogen Permeation in Zinc Plating Baths
The Influence of Phase Content on Steel Hydrogen Stability at Elevated Temperatures and Pressures
Moist Hydrogen Sulphide Corrosivity
Primary and Secondary Water Chemistry on PWR Nuclear Power Plant
Corrosion of Steel Pipes by Potable Water
Studies on Alkaline Cooling Water Treatment
Corrosion of Equipment in the Steam Circuit of a Fertilizer Plant
Stress Corrosion and Corrosion Fatigue Cracking Occurring in a Refinery Unit
A Study of Surface Film Formed on 316L Stainless Steel in Industrial Urea Media
Investigation of Corrosion Protection in the Fertilizer Industry
Corrosion Behaviour of Boiler Steel EN-24 in Sugarcane Ash
Diagnosis of Mechanical and Corrosion Wear in Sugar Industry
A Study of Steel Corrosion in Bleaching Environment of Pulp and Paper Industry
Corrosion in Coal Gasification Quench System: A Selected Review
Selection of Materials of Construction for Carboxylic Acids Mixture in the Waste Liquors and Corrosion Control by Anodic Protection
Electrochemical Behaviour and Field Performance of Stainless Steels in Urea Synthesis Environment
Behavior of Niobium in the Chlorine-Alkali Industry
Titanium, Tantalum, Zirconium and Niobium to Combat Corrosion in Chemical Industry
Pitting of Carbon Steel in Sweet Crude Oil Service
Stress Corrosion Cracking of Equipment in Chemical Process Industries
Corrosion Problems in Steam Turbines at Fossil and Nuclear Power Stations
Design of Anodic Protection System for Stainless Steel Heat Exchangers in Sulphuric Acid Industry
The Effect of Elemental Constituents of Steel on Corrosion and Hydrogen Evolution in Pickling Bath
Lowering General and Preventing Local Kinds of Corrosion of Process Equipment by Anodic and Cathodic Protection
Use of Special Stainless Steels in Indian Chemical Process Industries
Electrochemical Mechanism of Inhibiting the Corrosion of Metals with Oxyanions
Effect of Various Substituents in Furan on the Inhibitor Efficiency
Discussion on Corrosion Rate of High Concentration of Chloride Water and the Evaluation of Corresponding Inhibitors
An Investigation into Plant Materials as Corrosion Inhibitor for Hydrochloric Acid
Corrosion Inhibition of Alkyl Amines in Acid Solution
Study of the Mechanism of Inhibition of 3,5-Diaminobenzoic Acid towards the Corrosion of Mild Steel in in Hydrochloric Acid
Inhibition of the Corrosion of Iron and Steel in Acid Pickling Media by Nitrogen Containing Compounds
Sers and Impedance Study on Inhibition of Copper Corrosion in Sulfate Solutions by Benzotriazole and its Derivatives
Adsorption and Corrosion Inhibition Effect of Polar Organic Compounds on Iron in HCl-HClO4 Solutions
Corrosion Inhibition of Mild Steel in Pickling Acids by Ethoxylated Unsaturated Fatty Acids
Adsorption of Aliphatic Amines on Iron Surface Form Acidic Solutions
Corrosion Inhibition of 304 Stainless Steel in H3PO4/Cl Solutions by Metallic Cations
The Synergetic Effect of Ethanolamine and Benzotriazole on the Corrosion Inhibition of Copper
Effect of Structure Parameters of Organic Inhibitors on their Efficiency in Inhibiting Corrosion of Steel in Hydrocarbon/Electrolyte System
Factors of Corrosion Inhibition of Stainless Steels and Fe-Ni Alloys by Chloride in H2SO4
Inhibiteurs De La Corrosion Du Cuivre Par L'Eau De Gabes "Sud Tunisein"; Leur Mode D'Action
Study of the Kinetics and Mechanisms of Pitting Inhibition by Chromate of 304 Stainless Steel in Chloride Solutions
Inhibition of Corrosion of Mild Steel in Sea Water Using Gluconates
Plastics Containing Corrosion Inhibitios
Corrosion Protection
Corrosion Protection
Triazole Derivates and Similar Compounds as Corrosion Inhibitors for Copper
The Influence of Benzotriazole on the Resistance of Mild Steel to Localized Attack in Chloride Solutions
Investigations on Copper Corrosion Inhibitors
Effect of S-Sbenzyl Thiouronium Chloride on the Corrosion of Mild Steel in HCl Solution
Acetylinic Alcohols as Inhibitors for Nickel in Hydrochloric Acid Solutions
Impedance Studies in Neutral Inhibitive Media
The Effect of some Inhibitors on Mechanical Relationships of Metals and their Corrosion in Acids
Synergistic Effect of Dicyclo Hexylamine - with Halide Ions on the Corrosion of Mild Steel in Sulphuric Acid Medium
Non-Heavy Metallic Inhibitor for Control of Corrosion and Fouling in an Ammonia Cooling Water System
Synergistic Effects of Halide Ions and Benzyl Amine on Electrochemical Behaviour of Mild Steel in Dilute Sulfuric Acid
On the Nature of Surface Compounds Using Sulphurated Inhibitors
The Effet of the Inhibitor Dedc on the Sulphide Induced Attack on Aluminium Brass and Cupronickel Alloys in Flowing Synthetic Sea Water
Hydrazine and Substituted Hydrazines as Corrosion Inhibitors for Mild Steel in Alkaline Mine Water
Acridine and Quinolines as Acid Corrosion Inhibitors for Copper
Inhibitors Study against Corrosion in Hydrocarbon Mixers
A Theoretical Approach to the Mechanism of Pitting Initiation I. the Thermodynamics of Pitting Initiation
A Theoretical Approach to the Mechanism of Pitting Initiation II. the Kinetics of Pitting Initiation
Research on Knife-Line Attack Resisting Properties of Cr17Ni2 Steel Weld Joint
The Relationship between the Propagation Rate of Localized Corrosion and the Electrode Potential of Local Anode of Steels for Offshore Platform
Crevice Corrosion of Stainless Steel in High Temperature Chloride Solutions
Stainless Steels Crevice Corrosion in Geothermal Waters
Electrochemical Aspects of the Growth of Corrosion Pits in Stainless Steels
The Relative Susceptibility of P/M and I/M Al-Zn-Mg Alloys to Pitting Corrosion and Stress Corrosion Cracking in 3.5% NaCl
Pitting Corrosion of Austenitic Stainless Steels with Chemically Treated Surfaces
Investigation on Crevice Width Influencing Chemical and Electrochemical Parameters of the Solution in the Crevice
Some Aspects of the Initiation Phase of Crevice Corrosion of Stainless Steel in Chloride Solution
The Influence of the Fresh Cooling Water Component on the Pitting Corrosion of Brass Tubes
Stability of Localized Corrosion Processes
Correlation between Solvation Effects and Pitting Corrosion of Ti6Al4V in Methanolic Media
Corrosion Behaviour of Conductive Lines of Al-Cu on Oxidized Silicon Wafers
Prevention of Pitting Corrosion of Aluminium Easy-Open Ends of TFS Cans
A New Method of Pitting Potential Determination
Corrosion Behaviour of the 8090 Aluminium Lithium Alloy in Chloride Solutions
Correlation between Long Time and Short Time Tests to Detect Pitting and Exfoliation Corrosion in Al-Li (8090) Alloy
Pitting, Crevice and Intergranular Corrosion Resistance of Titanium Modified Austenitic Stainless Steels
Influence of Carbon Content on the Pitting Corrosion Behaviour of Thermally Aged Type 316 Stainless Steel Welds
Pitting Nucleation in Austenitic Stainless Steels
On the Origin of Pitting Induction Time
Corrosion Behaviour of Cu-Ni Alloys in Sea Water at Different Hydrostatic Pressures
Seawater Corrosion Behaviour of Steels with Varying Amounts of Copper
Effects on Variations in Biofouling Assemblage and Exposure Conditions on the Corrosion of Mild Steel
Corrosion Characterization of Tungsten Alloys in Marine Environments
Corrosion Behaviour of SUS 329J1 Stainless Steel in Acetic Acid Solutions
Sulphidation of Monocrystalline Cu-6, 5% Al Alloy in Liquid Sulphur at 717° K
Corrosion of Copper by Food Acids Containing Colourants and Sweetening Agents. Part V. Corrosion by Acetic Acid
Corrosion of Austenitic Stainless Steel by Liquid Sodium and by Reactor Fuel in Fast Breeder Reactors
Anodic Dissolution of Iron in Organic Solvents
Studies on some Solid State Reactions Relevant to Hot Corrosion
The Effect of Niobium on the Hot Corrosion Behaviour of Nickel-Base Superalloy
The Stresses of Oxide Scale of Nb and Nb Alloy during High Temperature Oxidation
Influence of Reactive Element Addition on the Protectivity of Al2O3 Scales Formed on Fe-Cr-Al Base Alloys
Bistability in High Temperature Corrosion Processes
Oxidation of Copper in SO2+O2 Atmosphere at 1100-1230K
Sodium Sulphate Induced Hot Corrosion of Pure Fe, Mn and Cr in Combustion Gas
Effect of Sulphate Anion on Anodic Breakdown of Oxidized Fe, Ni and Cr in Fused NaCl-KCl Eutectic at 700°C
The Corrosion and Abrasion Attack of Molten Zinc on the Bath Wall during Hot-Dipping
Application of Acoustic Emission Technique in High Temperature Oxidation Studies
Effect of Various Heat-Treatments on the Oxidation Behaviour of 2 1/4 Cr-1 Mo Steel
Effect of Cold Work on the Oxidation Resistance of Ferritic Steels
Corrosion Behaviour of Pure Titanium and Ti-6.6 Al-2.9 Mo-1.7 Zr-0.23 Si Alloy in NaCl and Na2SO4
Oxidation Kinetics of Cu-Zr Alloys
Sulphidation Studies of Fe-15, Cr-4 Al Alloy with Y and Zr Additions at 850°C
Effect of Zirconium on Isothermal and Cyclic Oxidation of Fe-15wt% Cr-4wt% Al Alloy in the Temperature Range of 1000-1300°C
Oxidation of Pure Zirconium in Pure Oxygen in Temperature Range 400-850°C
Hot Corrosion of Nickel and Cobalt Base Alloys at Intermediate Temperatures
Combined or Successive Effect of a Strain and of Oxidation of an NiCr-16 Fe-8 Alloy
Oxidation Behaviour of Superalloys Protected by Plasma Sprayed M Cr AlYTa Coatings
Improvement of Oxidation Resistance of Heat-Resistant Steel by Ion Beam Mixing
Study on Corrosion Products of IN657 Alloy in Molten Salts
Fireside Corrosion Phenomena in Superheaters of Coextruded Materials with 18, 25, 35 and 50% Cr at Metal Temperatures of up to 700°C
Studies on Non-Isothermal Oxidation Behaviour of Iron and Iron-Chromium Alloys
Effect of Interrupted and Uninterrupted Imptessed Direct Current on the Oxidation Behaviour of Copper at High Temperatures
The Properties of Protective Scales on Surface Modified Stainless Steel towards Sulphidation at High Temperatures
Study of Oxidation Behaviour of Modified 9 Cr-1 Mo Ferritic Steel at Elevated Temperatures and Pressures
High Temperature Hot Corrosion Control by Fuel Additives (Contaminated Fuels)
High Temperature Corrosion of a Ni-Base Superalloy by Vanadium
Laser Surface Alloying or Coating of Metals to Protect against High Temperature Corrosion
Co-Deposition of Cr and Al by Pack Cementation and the Resistance of such Coatings against Oxidation and Hot Corrosion
Corrosion and Oxidation Resistance of Zinc Composite Materials
Corrosion Behaviour of Steel and Stainless Steel in Hot Carbonate Solutions
Hot Corrosion Behavior of Platinum Modified Coatings
The Influence of Implanted Yttrium and Lanthanum on Morphology of Alumina Scale Grown on Beta-NiAl Intermetallic Compound
Anodic Polarization of Iron, Chromium and Steel 15 x 28 in Molten Alkali Carbonates at 1073 K
Influence of Sulphur on Oxidation of Ni66 Cr34 and Ni80 Cr20 Alloys
The Effect of Superficial Aluminization on the Corrosion of the Steel Fe 2.25 Cr1 Mo in Different Oxidizing and/or Sulphidizing Atmospheres
Corrosion and Electrochemical Study on 316L (Urea Grade) Stainless Steel in Urea Solution under High Temperature and Pressure
Beneficial and Detrimental Effects of Silica in the High Temerature Oxidation of 20Cr/25Ni/Nb Stainless Steel
Reaction of Stainless Steel with Liquid Potassium Containing Dissolved Oxygen
The Behaviour of some Super Alloys in Different High Temperature Atmospheres
Some Thermodynamic Investigations on the Ternary Oxygen Compounds of Relevance in the Corrosion of Sodium-Steel Systems
Carburization of Steel in Liquid Sodium and the Nature of the Carbon-Bearing Species
Anodic Behaviour of Titanium and Titanium Alloys in H2SO4 Solutions - Influence of some Inhibitors
Influence of the Structure of Protective Films on the Mechanical Breakdown of Passivity
The Passivation of Chromium
"In-Situ" Laser Raman Spectroscopy Studies of Corrosion Film on Metals in High-Temperature Aqueous Environments
Ellipsometric Investigation of Passive Films Formation on Two Iron-Nickel Alloys
Effects of Calcium Ions on the Morphology and Corrosion Resistance of Zinc-Phosphated Steel
Etching Properties of the Indium Tin Oxide
Deterministic Models for the Distributions in Passivity Breakdown Parameters
Potentiodynamic and Galvanostatic Passivity Measurements. A General Quantitative Interpretation: The Niobium Case
The Secondary Passivating Film on Tin in Sodium Perchlorate Solutions. Its Reduction Peak
The Reduction of Sn(II) Passivating Film on Tin before and after the Growth of the Sn(IV) Passivating Film
Passivation and Stability of Passive State of Chrome-Nickel Austenitic Steels Depending on Molybdenum Content an MnS Inclusions
Kinetics of Passivation of Stainless Steels in Chloride Solutions
The Passivating Films of Zinc in Alkaline Solution
Breakdown of the Passive Film on Nickel and Nickel Alloys Induced by Sulphur
Application of Impedance Technique to the Interpretation of the Role of Alloying Tungsten on the Passivity of Stainless Steels
Ellipsometric Study of Passive Films Formed on a Duplex Stainless Steel in Chloride Solution
Electrochemistry of Chromium
Influence of Alloying Components on Passivation of Titanium and Aluminium Alloys in Molten Alkali Carbonates
Study of the Passivation Kinetics of Zircaloy 4 in Chloride Containing Aqueous and Hydroorganic Solutions
Esca and Impedance Study of Passive Films on Mo-Containing Stainless Steels
The Role of Silicon in the Corrosion of Stainless Steels in Nitric Acid Solutions
The Inflection Point Method with Inter 1 Code
A Technique for Measurement of Differential Polarization Resistance
Development of a Field Monitoring Method for the Protective Properties of Rust and Paint Films on Steel Structures
AC Impedance of Iron in Sulfuric Acid Medium Measured by Laplacian Transformation Method
Applicability of EPR Technique for Assessing Intergranular Corrosion Susceptibility of Cold Worked Type 304 SS
Erosion of Metals in High Speed Mist Flow Evaluation of Thereshold Velocity by Acoustic Emission System
The Determination of Corrosion Rates by Analysis of Inflection Point Data
Electrochemical Noise Corrosion Monitoring Method in Laboratory Use
Relaxation Techniques for Measurement of Corrosion Rate
A New Three Electrode Direct Reading Digital Corrosion Meter
A Technique for Measuring Adsorption of Gases on Flat Surfaces
Corrosion of Nickel in Acids - an Accelerated Tafel Plot Study
Evaluation of Faradaic Distortion Method for Corrosion Rate Measurements
Atmospheric Corrosion Monitoring by Hydrogen Permeation Technique
Monitoring of Corrosion and Wear Debris for Better Management of Equipment
A.C. Impedance Measurements for Characterizing the Electrochemical Behaviour of AA 3003 in Engine Coolants